HW6160

Material overview

A heat-resistant prototyping system with a specified post-curing process.

This system requires a defined curing and post-curing process for thermal performance. Discuss the required temperature, exposure duration and part geometry with Haiwoo.

Tell us the intended application, part geometry and material behaviour you need. Request the current technical and safety information before mixing or casting. Descriptions such as ABS-like and PP-like refer to prototype behaviour.

Material information

Material / process

Vacuum casting

Mixing ratio

100:200 by weight
A : B. Weigh components for the selected system.

Hardness

80–82 Shore D
ISO 868. Confirm specimen and cure conditions with the current technical data.

Flexural modulus

2100–2200 MPa
ISO 178. Confirm specimen and cure conditions with the current technical data.

Flexural strength

108–120 MPa
ISO 178. Confirm specimen and cure conditions with the current technical data.

Tensile strength

60–70 MPa
ISO 527. Confirm specimen and cure conditions with the current technical data.

Elongation at break

15–16 %
ISO 527. Confirm specimen and cure conditions with the current technical data.

Request the technical and safety data for this material, including processing parameters and test conditions.

Supply & material preparation

Confirm the selected formulation, component packaging, quantity, destination and lead time with your quotation. Sample format and availability are agreed individually.