HW223

Material overview

A heat-resistant prototyping system. Suitability depends on the curing schedule and test conditions.

This system requires a defined curing and post-curing process for thermal performance. Discuss the required temperature, exposure duration and part geometry with Haiwoo.

Tell us the intended application, part geometry and material behaviour you need. Request the current technical and safety information before mixing or casting. Descriptions such as ABS-like and PP-like refer to prototype behaviour.

Material information

Material / process

Vacuum casting

Mixing ratio

100:80 by weight
A : B. Weigh components for the selected system.

Hardness

78–82 Shore D
Test method is not specified in the source sheet. Confirm specimen and cure conditions with the current technical data.

Flexural modulus

2300 MPa
Test method is not specified in the source sheet. Confirm specimen and cure conditions with the current technical data.

Flexural strength

80 MPa
Test method is not specified in the source sheet. Confirm specimen and cure conditions with the current technical data.

Tensile strength

60–62 MPa
Test method is not specified in the source sheet. Confirm specimen and cure conditions with the current technical data.

Elongation at break

13–15 %
Test method is not specified in the source sheet. Confirm specimen and cure conditions with the current technical data.

Request the technical and safety data for this material, including processing parameters and test conditions.

Supply & material preparation

Confirm the selected formulation, component packaging, quantity, destination and lead time with your quotation. Sample format and availability are agreed individually.